UNIT |
VALUE |
ASTM
|
| Specific Gravity |
-------- |
1.17 - 1.174 |
D 792 |
| Melt Flow Rate @ 220 °C / 10 kg |
g/10 min |
20 min |
D 1238 |
| Molding Shrinkage 3.2 mmsection |
% |
0.40 - 0.60 |
D 955 |
| MECHANICAL |
| Impact Strength, Izod |
|
| notched 1/8 in (3.2 mm) section |
J/m |
80 min |
D 256 |
| Tensile Strength @ 50mm/min |
MPa |
44 min |
D 638 |
| Tensile Elongation@ yield 50mm/min |
% |
> 8.0 |
D 638 |
| Flexural Strength 2mm/min |
MPa |
50 min |
D 790 |
| Flexural Modulus 2mm/min |
MPa |
1800 min |
D 790 |
| THERMAL |
| Heat Deflection Temperature |
|
| @ 264 psi (1820 kPa) |
°C |
82 min |
D 648 |
| Vicat Softening- Method B |
°C |
96 Min |
D 648 |
| Flammability @ 3mm |
------ |
V0 |
UL94 |
GENERAL PROCESSING FOR INJECTION MOLDING |
Injection Pressure |
MPa |
|
|
Melt Temperature |
°C |
|
|
Mold Temperature |
°C |
|
|
Drying |
hr @ °C |
|
|
Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.The Above mentioned tchnical data is purely indicative and is given without any guarantee. |
GLS POLYMERS PVT LTD,#415,11th CROSS,4th PHASE, PIA, BANGALORE-560 058, INDIA |